AISI 410
| C (%) | Mn (%) | Si (%) | Cr (%) | Ni (%) | P (%) | S (%) | Cu (%) | N (%) |
0.018 |
0.38 |
0.3 |
12.2 |
0.1 |
0.016 |
0.001 |
0.03 |
0.02 |
AISI 430
| C (%) | Mn (%) | Si (%) | Cr (%) | Ni (%) | P (%) | S (%) | Cu (%) | N (%) |
0.11 |
0.38 |
0.3 |
16.15 |
0.1 |
0.016 |
0.001 |
0.03 |
0.02 |
AISI 202
| C (%) | Mn (%) | Si (%) | Cr (%) | Ni (%) | P (%) | S (%) | Cu (%) | N (%) |
0.88 |
10.7 |
0.7 |
17.08 |
4.15 |
0.036 |
0.028 |
0.04 |
0 |
AISI 205
| C (%) | Mn (%) | Si (%) | Cr (%) | Ni (%) | P (%) | S (%) | Cu (%) | N (%) |
0.105 |
15.4 |
0.52 |
12.7 |
2.06 |
0.029 |
0.028 |
0.03 |
0 |
AISI 304
| C (%) | Mn (%) | Si (%) | Cr (%) | Ni (%) | P (%) | S (%) | Cu (%) | N (%) |
0.065 |
1.1 |
0.6 |
18.03 |
8.02 |
0.036 |
0.012 |
0 |
0.04 |
Fiziksel özellikler
| Tane şekli | Silindirik veya yuvarlak |
| Sertlik | 308-509 HV (boyut & tane şekline bağlı olarak) |
| Çekme dayanımı | 490-1520 Mpa |
| Mikroyapı | AISI 304: Deforme Austenit AISI 430/410: Deforme Ferrit |
| Yoğunluk | 7,8 g/cm³ |
| Yığın yoğunluğu | 4,5 g/cm³ |